Continuous electroconversion of CO2 into formate using 2 nm tin oxide nanoparticles

Abstract : Tin oxide nanoparticles (SnO 2 NPs) as electrocatalyst for the production of formate from CO 2 reduction reaction (CO 2 RR). We synthesize, characterize and evaluate high surface area SnO 2 NPs (2.4 nm and 299 m 2 g-1 in diameter size and surface area, respectively), for the continuous production of formate at high current density within a flow electrolyzer. SnO 2 NPs under Ar and CO 2 reduction conditions were studied by cyclic voltammetry. SnO 2based gas diffusion electrodes (SnO 2-GDEs) were manufactured to perform continuous CO 2 RR. A maximum formate concentration value of 27 g L-1 was achieved with a Faradaic efficiency (FE) of 44.9% at 300 mA cm-2 , which was significantly stable and reproducible when operated up to 10 h. Nevertheless, ohmic drop contribution due to the semiconducting properties of SnO 2 was not negligible. The low total FE (< 60%) of products pointed out a leakage of formate by crossover migration through the membrane from the catholyte towards the anolyte.
Document type :
Journal articles
Complete list of metadata

https://hal.sorbonne-universite.fr/hal-03267685
Contributor : Véronique Martin Connect in order to contact the contributor
Submitted on : Tuesday, June 22, 2021 - 3:53:39 PM
Last modification on : Monday, December 6, 2021 - 4:18:03 PM
Long-term archiving on: : Thursday, September 23, 2021 - 6:52:59 PM

File

 Restricted access
To satisfy the distribution rights of the publisher, the document is embargoed until : 2021-12-15

Please log in to resquest access to the document

Identifiers

Citation

Ivan Merino-Garcia, Lionel Tinat, Jonathan Albo, Manuel Alvarez-Guerra, Angel Irabien, et al.. Continuous electroconversion of CO2 into formate using 2 nm tin oxide nanoparticles. Applied Catalysis B: Environmental, Elsevier, 2021, 297, pp.120447. ⟨10.1016/j.apcatb.2021.120447⟩. ⟨hal-03267685⟩

Share

Metrics

Record views

124